AquaSys® 120

Starting at: €100

REQUEST QUOTE

AquaSys® 120

Starting at: €100

1.75mm diameter

500g spool

 

$100

 

Dims: 23 x 21 x 6 cm

Diameter: 1.75MM

Volume: 500g

Weight: 0.93kg

Extruder temperature: 220-245ºC

Build plate temperature: Up to

RT-130ºC

Chamber temperature: 80-120ºC

1.75mm diameter

1kg spool

 

$180

 

Dims: 23 x 21 x 8 cm

Diameter: 1.75MM

Volume: 1kg

Weight: 1.5Kg

Extruder temperature: 220-245ºC

Build plate temperature: Up to

RT-130ºC

Chamber temperature: 80-120ºC

2.85mm diameter

500g spool

 

$100

 

Dims: 23 x 21 x 6 cm

Diameter: 2.85MM

Volume: 500g

Weight: 1.0kg

Extruder temperature: 220-245ºC

Build plate temperature: Up to

RT-130ºC

Chamber temperature: 80-120ºC

2.85mm diameter

1kg spool

 

$180

 

Dims: 33 x 31 x 11 cm

Diameter: 2.85M

Volume: 1kg

Weight: 2.3kg

Extruder temperature: 220-245ºC

Build plate temperature: Up to
RT-130ºC

Chamber temperature: 80-120ºC

 

 

Glass, PEI

ABS, PC-ABS, PC, PA, PET, PETG, PA-CF. PA-GF, PET-CF, PET-GF, ASA, PVDF, PUT, TPE, CPE

Store in sealed bag in a cool, dry location when not in use. 

Print Head: 220-250ºC
Build Plate: 50-120ºC
Chamber: RT-120ºC

50-80ºC in agitated water. 100% water soluble.

The statements, technical information and recommendations contained herein are believed to be accurate as of the date hereof. Since the conditions and methods of use of the product and of the information referred to herein are beyond our control, Infinite Material Solutions, LLC. Expressly disclaims any and all liability as to any results obtained or arising from any use of the product or reliance on such information: NO WARRANTY OF FITNESS FOR ANY PARTICULAR PURPOSE, WARRANTY OF MERCHANTABILITY OR ANY OTHER WARRANTY, EXPRESSED OR IMPLIED, IS MADE CONCERNING THE GOODS DESCRIBED OR THE INFORMATION PROVIDED HEREIN. The information provided herein relates only to the specific product described and may not be applicable when such product is used in combination with other materials or in any process. The user should thoroughly test any application before commercialization. Nothing contained herein constitutes a license to practice under any patent and it should not be construed as an inducement to infringe any patent and the user.